表 3 具有不同墨水含量的光子晶体薄膜的 a 和 b 值
*
*
Table 3 a and b values of photonic crystal films with different contents of ink
墨水质量 10∶0 7∶3 5∶5 3∶7 0∶10
分数/% a * b a b a * b a b a * b *
*
*
*
*
*
*
0 –1.44 3.51 –1.68 1.02 –2.95 0.89 –4.08 –0.98 –8.79 –3.47
0.03 –1.63 13.99 –2.11 2.72 –3.08 3.26 –6.94 –1.40 –12.21 –3.48
0.06 –1.68 20.52 –2.18 3.94 –3.66 3.49 –7.00 –1.48 –14.19 –3.54
0.09 –2.12 21.84 –3.44 4.14 –4.16 3.89 –9.14 –3.08 –20.36 –4.22
色差 偏绿 偏黄 偏绿 偏黄 偏绿 偏黄 偏绿 偏蓝 偏绿 偏蓝
注：比例均为 m(S A)∶m(S B)。

3 结论 microspheres[J]. Fine Chemicals (精细化工), 2020, 37(4): 853-859.
[9] PURSIAINEN O L, BAUMBERG J J, WINKLER H, et al.
Nanoparticle-tuned structural color from polymer opals[J]. Optics
采用基于 Stöber 工艺的溶剂调控法合成了 285 和 Express, 2007, 15(15): 9553-9561.
[10] TAKEOKA Y, YOSHIOKA S, TAKANO A, et al. Production of
247 nm 两种不同粒径的均匀 SiO 2 粒子，将两种 SiO 2
colored pigments with amorphous arrays of black and white colloidal
粒子分别按质量比 10∶0、7∶3、5∶5、3∶7、0∶ particles[J]. Angewandte Chemie, 2013, 52(28): 7261-7265.
[11] STÖBER W, FINK A. Controlled growth of monodisperse silica
10 超声混合，通过重力沉降自组装法制备可调控光 spheres in the micron size range[J]. Journal of Colloid and Interface
子晶体结构色薄膜。为解决薄膜颜色较浅问题，将 Science, 1968, (26): 62-69.
[12] ZHOU L, WU Y J, LIU G J, et al. Fabrication of high-quality silica
墨水添加至 SiO 2 粒子悬浮液中，由于墨水中存在的 photoniccrystals on polyester fabrics by gravitational sedimentation
炭黑粒子，使得薄膜的明度降低，色度提高。实验 self-assembly[J]. Coloration Technology, 2015, 131(6): 413-423.
[13] GAO W H, RIGOUT M, OWENS H. Facile control of silica
还确定了最佳墨水质量分数为 0.06%，此时薄膜亮 nanoparticles using a novel solvent varying method for the fabrication
度较低，色度最高，结构色的对比度和饱和度最好。 of artificial opal photonic crystals[J]. Journal of Nanoparticle Research,
2016, 18(12): 1-10.
本研究通过混合两种不同粒径的 SiO 2 粒子成功构建 [14] GAO W H, RIGOUT M, OWENS H. Self-assembly of silica colloidal
了不同颜色的结构色材料，不需要制备各种粒径的 crystal thin films with tuneable structural colours over a wide visible
spectrum[J]. Applied Surface Science, 2016, 380(1): 12-15.
SiO 2 ，仅通过改变混合比例即可得到多种颜色，其 [15] GAO W H, RIGOUT M, OWENS H. The structural coloration of
工艺优于传统的制备方法。此方法简单高效，结构 textile materials usingself-assembled silica nanoparticles[J]. Journal
of Nanoparticle Research, 2017, 19(9): 1-11.
色不仅易调控还具有低角度依赖性，可广泛应用于 [16] GAO W H, RIGOUT M, OWENS H. Optical properties of cotton
光子晶体颜料、智能生色、防伪印刷、包装、纺织 and nylon fabrics coated with silica photonic crystals[J]. Optical
Materials Express, 2017, 7(2): 341-353.
服装等相关领域。 [17] PENG J J (彭晶晶), CHEN J Y (陈佳颖), GAO W H (高伟洪), et al.
Synthesis of uniform SiO 2 nanoparticles and its structural coloration[J].
参考文献： Journal of Beijing Institute of Fashion Technology (Natural Science
Edition) (北京服装学院学报: 自然科学版), 2021, 41(1): 7-13.
[1] YABLONOVITCH E. Inhibited spontaneous emission in solid-state [18] CHEN J Y (陈佳颖), TIAN X (田旭), PENG J J (彭晶晶), et al.
physics and electronics[J]. Physical Review Letters, 1987, 58(20): Fabrication of structural colors for knitted fabrics[J]. Journal of
2059-2062. Textile Research (纺织学报), 2020, 41(7): 117-121.
[2] JOHN S. Strong localization of photons in certain disordered dielectric [19] WANG W T, TANG B T, MA W, et al. Easy approach to assembling
superlattices[J]. Physical Review Letters, 1987, 58(23): 2486-2489. a biomimetic color film with tunable structural colors[J]. Journal of
[3] ZHANG K Q (张克勤), YUAN W (袁伟), ZHANG A (张骜). the Optical Society of America A, 2015, 32(6): 1109-1117.
Structural color of photonic crystal[J]. Functional Materials Information [20] XIAO M, LI Y W, ALLEN M C, et al. Bio-inspired structural
(功能材料信息), 2010, 7(5): 39-44. colorsproduced via self-assembly of synthetic melanin nanoparticles[J].
[4] TIAN H R (田桓荣), LIU J Y (刘建勇). Research progress in structural ACS Nano, 2015, 9(5): 5454-5460.
chromogenic textiles[J]. Knitting Industries (针织工业), 2019, (1): [21] ZHANG Y F, DONG B Q, CHEN A, et al. Using cuttlefish ink as an
30-35. additive to produce non-iridescent structural colors of high color
[5] ZUO L N (左丽娜), PENG Y (彭瑜), GUO H H (郭贺虎), et al. visibility[J]. Advanced Materials, 2015, 27(32): 4719-4724.
Research progress of structural color construction based on multi- [22] LEE C H, YU J L, WANG Y M, et al. Effect of graphene oxide
dimensional photonic crystals and amorphous photonic crystals[J]. inclusion on the opticalreflection of a silica photonic crystal film[J].
Advanced Textile Technology (现代纺织技术), 2019, 27(6): 1-15. RSC Advances, 2018, 8(30): 16593-16602.
[6] CHEN J Y (陈佳颖), XIN B J (辛斌杰), XIN S F (辛三法), et al. [23] ZHANG H (张慧). Structural color appearance on the fabric by
Research progress in structurally colored fabrics using photonic monodisperse colloidal SiO 2 spheres[D]. Shanghai: Donghua University
crystals[J]. Journal of Textile Research (纺织学报), 2020, 41(4): (东华大学), 2017.
181-187. [24] HAN Y D (韩延东). Synthesis of nanostructured SiO 2 particles by
[7] ZENG Q (曾琦), LI Q S (李青松), YUAN W (袁伟), et al. The Stöber method[D]. Changchun: Jilin University (吉林大学), 2007.
mechanism and its application of amorphous photonic crystals with [25] TILLEY R J D. Colour and the optical properties of materials[M].
structural color[J]. Materials Reports (材料导报), 2017, 31(1): New York: John Wiley & Sons, 2010.
43-55. [26] LIU G J, ZHOU L, WU Y J, et al. Optical properties of three-
[8] ZHENG H L (郑宏亮), FANG Y C (方寅春), WANG C E (王翠娥), dimensional P(St-MAA) photonic crystals on polyester fabrics[J].
et al. Preparation of structural color fabrics of SiO 2@PDA Optical Materials, 2015, 42(1): 72-79.