Page 28 - 201811

·1814· 精细化工 FINE CHEMICALS 第 35 卷

表 2 不同 DVP 组分水性聚氨酯的 N—H 伸缩振动区分峰结果
Table 2 Peak fitting results of the N—H stretching vibration region of WPU films synthesized with different DVP contents
–1
出峰位置/cm 峰面积/%
样品
Free N—H Hydrogen bonded N—H Free N—H Hydrogen bonded N—H
WPU-0 3510 3329 33.37 66.63
WPU-1 3507 3327 29.22 70.78
WPU-2 3515 3329 31.77 68.23
WPU-3 3516 3329 32.91 67.09
WPU-4 3513 3328 33.08 66.92

表 3 不同 DVP 组分水性聚氨酯的 C==O 伸缩振动区分峰结果
Table 3 Peak fitting results of the C==O stretching vibration region of WPU films synthesized with different DVP contents
–1
出峰位置/cm 峰面积/%
样品 Hydrogen bonded Hydrogen bonded Hydrogen bonded Hydrogen bonded
Free C==O Free C==O
C==O of carbamate C==O of urea C==O of carbamate C==O of urea
WPU-0 1718 1693 1648 36.44 41.69 21.87
WPU-1 1718 1696 1644 24.23 48.55 27.22
WPU-2 1717 1696 1654 24.91 49.09 26.00
WPU-3 1719 1697 1646 25.16 50.62 24.22
WPU-4 1719 1698 1651 25.42 51.38 23.20

由表 4 和图 7 可知，不同组分 WPU 胶膜的热
重曲线都表现出近似相同的降解趋势，表明 DVP 的
加入并没有改变胶膜的热降解机理。由表 4 可知，
随着 DVP 含量的增加，不同组分 WPU 胶膜的 T 5%
和 T 50% 均先增后降。当 w（DVP）=0.5%时，T 5% 和
T 50% 分别为 269.9 和 343.5 ℃。

图 7 不同 DVP 组分水性聚氨酯胶膜 TG 曲线
Fig. 7 TG curves of WPU films with different DVP contents

由图 8 可知，胶膜热分解主要分 230~340 ℃及
340~410 ℃两个阶段，主要是以氨基甲酸酯结构为
主的裂解，且 325 ℃处为氨基甲酸酯键的降解；在
340~410 ℃内，主要是以 WPU 胶膜软段的热解离。

图 6 不同 DVP 组分水性聚氨酯乳液粒径分布图
Fig. 6 Particle size and particle size distribution of WPU
emulsions synthesized with different DVP contents

表 4 不同 DVP 组分水性聚氨酯胶膜的特征失重温度
Table 4 Characteristics weight loss temperature of the films
synthesized with different DVP contents
w(DVP)/%

0 0.5 1.0 1.5 2.0

T 5%/℃ 267.0 269.9 271.8 264.8 262.6
图 8 不同 DVP 组分水性聚氨酯胶膜 DTG 曲线
T 50%/℃ 336.2 343.5 346.1 335.4 333.5 Fig. 8 DTG curves of WPU films with different DVP contents