Page 92 - 《精细化工》2020年第8期

·1590· 精细化工 FINE CHEMICALS 第 37 卷

图 4 γ-Al 2 O 3 (a)、γ-Al 2 O 3 -C1 (b)、γ-Al 2 O 3 -C2 (c)、γ-Al 2 O 3 -C3 (d)、γ-Al 2 O 3 -iso-C3 (e)、γ-Al 2 O 3 -C4 (f)、γ-Al 2 O 3 -sec-C4 (g)、
γ-Al 2 O 3 -iso-C5 (h)、γ-Al 2 O 3 -C6 (i)的 SEM 图
Fig. 4 SEM images of γ-Al 2 O 3 (a), γ-Al 2 O 3 -C1 (b), γ-Al 2 O 3 -C2 (c), γ-Al 2 O 3 -C3 (d), γ-Al 2 O 3 -iso-C3 (e), γ-Al 2 O 3 -C4 (f),
γ-Al 2 O 3 -sec-C4 (g), γ-Al 2 O 3 -iso-C5 (h) and γ-Al 2 O 3 -C6 (i)

图 5 加入不同有机醇制备 γ-Al 2 O 3 样品的氮气吸脱附曲线 图 6 加入不同有机醇制备 γ-Al 2 O 3 样品的孔径分布图
Fig. 5 Nitrogen adsorption and desorption curves of samples Fig. 6 Pore size distribution diagrams of samples prepared
prepared by adding different organic alcohols by adding different organic alcohols

表 1 加入不同有机醇制备样品的比表面积、孔容、孔径数据
Table 1 Specific surface area, pore size and pore volume data of samples prepared by adding different organic alcohols

γ-Al 2O 3 γ-Al 2O 3-C1 γ-Al 2O 3-C2 γ-Al 2O 3-C3 γ-Al 2O 3-iso-C3 γ-Al 2O 3-C4 γ-Al 2O 3-sec-C4 γ-Al 2O 3-iso-C5 γ-Al 2O 3-C6
2
比表面积/(m /g) 243.8 247.7 231.9 255.9 250.0 247.7 231.9 214.2 270.9
3
孔容/(cm /g) 0.45 0.42 0.40 0.43 0.41 0.44 0.43 0.41 0.44
孔径/nm 5.83 5.41 5.27 5.33 5.22 5.54 5.50 5.31 5.19

2
由图 5 可以看出，所有样品的氮气吸脱附曲线 270.9 m /g。从孔径分布图（图 6）中可以看出，加
中均为典型的Ⅳ型等温线，具有明显的 H2 型磁滞 入不同碳链长度的醇后，孔径分布变窄，分布于
回线。其中，γ-Al 2 O 3 -C6 样品具有最大比表面积 2~12 nm 之间，为典型的介孔结构，这为得到较窄